Bob, if you forge wrought iron you need to forge it at a yellow heat to keep it from splitting.
No, that wrought iron was made in 1903.
Not forged at all. If you forge wrought iron the grain structure will refine and you lose the deffinition.
It's just stock removal from some flat material.